... STEEL . * By RALPH H. SHERRY , M.A. 3 CONSIDERABLE attention has been given in recent years to the phenomenon of coarse crystallisation or grain - growth in pure iron and . low - carbon steels permanently deformed and annealed . While ...
... STEEL . * By RALPH H. SHERRY , M.A. 3 CONSIDERABLE attention has been given in recent years to the phenomenon of coarse crystallisation or grain - growth in pure iron and . low - carbon steels permanently deformed and annealed . While ...
Strona 4
... steel , which was turned down into a double cone - shaped test - piece , similar to the tapered tensile test pieces mentioned . This bar was then partially decarbonised by ore annealing , and after cooling was pulled to fracture and ...
... steel , which was turned down into a double cone - shaped test - piece , similar to the tapered tensile test pieces mentioned . This bar was then partially decarbonised by ore annealing , and after cooling was pulled to fracture and ...
Strona 5
... Steels . Jan. 5 , 1917 TABLE I. -Forging Tests on Hot - rolled Rod . Grain - size in mm . at edge after one hour at 700 ... steel is : Carbon , o 08 ; manganese , 034 ; sulphur , o'032 ; phosphorus , o oro ; and silicon , 0'020 per cent ...
... Steels . Jan. 5 , 1917 TABLE I. -Forging Tests on Hot - rolled Rod . Grain - size in mm . at edge after one hour at 700 ... steel is : Carbon , o 08 ; manganese , 034 ; sulphur , o'032 ; phosphorus , o oro ; and silicon , 0'020 per cent ...
Strona 6
... steel . Refining took place only at 900 ° C. purest bromine and purified by many crystallisations . ( 1650 ° F. ) , no " critical " strain being noted . The material For the other experiments material was purified with was too light for ...
... steel . Refining took place only at 900 ° C. purest bromine and purified by many crystallisations . ( 1650 ° F. ) , no " critical " strain being noted . The material For the other experiments material was purified with was too light for ...
Inne wydania - Wyświetl wszystko
Kluczowe wyrazy i wyrażenia
acetic alcohol alkali ammonia amount amylase analysis analytical annealing apparatus application atomic B.Sc boiling British calcium carbon cent Chem CHEMICAL NEWS Office chemistry chemists chert chloride colloidal colour compounds concentration containing copper crystallisation determined dilute dissolved distilled dyes dysprosium engineering erbium evaporated experiments Explosives Farringdon Street ferric filtered fractions glass grains grms heat hydrochloric acid hydrogen hydrogen peroxide hydroxide increase industry Institution iron J. J. THOMSON Journ Laboratory lead liquid London maltose manufacture material matter metal method mixture molar Newcastle Street nickel nitrate nitric acid nitrile nitrogen obtained oxide oxidising paper peroxide phosphate potassium precipitate present production Prof pure pyrites reaction reagent Research salt samples Society sodium sodium hydroxide soil soluble solution starch steel substances sulphate sulphide sulphuric acid superphosphate supply Table temperature tion toluene trinitrotoluene velocity volume weight zinc ΙΟ