Chemical News and Journal of Industrial Science, Tomy 115-116Chemical news office., 1917 |
Z wnętrza książki
Wyniki 1 - 5 z 100
Strona 5
... Table I. TABLE III . - Quantitative Effect of Drawing and Annealing. Original rod Forged cold Forged cold Forged from 900 ° C. to red Sime . Spot next to anvil Forged from goo ° C. to black Forged from 90 ° C. to about 500 ° C 0'40 to ...
... Table I. TABLE III . - Quantitative Effect of Drawing and Annealing. Original rod Forged cold Forged cold Forged from 900 ° C. to red Sime . Spot next to anvil Forged from goo ° C. to black Forged from 90 ° C. to about 500 ° C 0'40 to ...
Strona 6
TABLE III . - Quantitative Effect of Drawing and Annealing Rod 0 · 320 in . Diameter . After drawing . Grain - size in mm . after one hour at 700 ° C. ( 1290 ' F. ) o 28 to 0'56 ; 800-850 ° C. ( 1470-1560 F. ) . 0'02 d Diam . In . Red ...
TABLE III . - Quantitative Effect of Drawing and Annealing Rod 0 · 320 in . Diameter . After drawing . Grain - size in mm . after one hour at 700 ° C. ( 1290 ' F. ) o 28 to 0'56 ; 800-850 ° C. ( 1470-1560 F. ) . 0'02 d Diam . In . Red ...
Strona 9
... TABLE I. - Cadmium . R'Fe ( SO4 ) 2 , 0.05 molar . H2SO4 , 0'01 molar . K. I. C = 50 · 00 580 560 540 7 6 6 520 6 500 480 460 6 C 6 0'47 2.78 6 4'73 6.72 3.96 872 10.69 12 69 393 4'04 14:61 4'11 4'06 3'94 4.18 3.93 4'04 4'ΟΙ 4 II 4:09 4 ...
... TABLE I. - Cadmium . R'Fe ( SO4 ) 2 , 0.05 molar . H2SO4 , 0'01 molar . K. I. C = 50 · 00 580 560 540 7 6 6 520 6 500 480 460 6 C 6 0'47 2.78 6 4'73 6.72 3.96 872 10.69 12 69 393 4'04 14:61 4'11 4'06 3'94 4.18 3.93 4'04 4'ΟΙ 4 II 4:09 4 ...
Strona 10
... Table I. Here , and in all the fol- between a solid and a dissolved substance will never towing tables , k , is the observed velocity constant uncor- represent , even approximately , the true rate of the chemi - rected , k is the same ...
... Table I. Here , and in all the fol- between a solid and a dissolved substance will never towing tables , k , is the observed velocity constant uncor- represent , even approximately , the true rate of the chemi - rected , k is the same ...
Strona 16
... TABLE V. - Properties of some Coarse - grained Hot - rolled Sheet . Thickness , E. L. , lb per M. S. , lb. , per Elong . , 2 in . per cent . Grain- size , mm . in . sq . in . sq . in . 0'096 23,000 46,000 0'20 0'093 26,300 50,000 ΟΙΟ ...
... TABLE V. - Properties of some Coarse - grained Hot - rolled Sheet . Thickness , E. L. , lb per M. S. , lb. , per Elong . , 2 in . per cent . Grain- size , mm . in . sq . in . sq . in . 0'096 23,000 46,000 0'20 0'093 26,300 50,000 ΟΙΟ ...
Inne wydania - Wyświetl wszystko
Kluczowe wyrazy i wyrażenia
acetic alcohol alkali ammonia amount amylase analysis analytical annealing apparatus atomic B.Sc British calcium carbon cent Chem CHEMICAL NEWS Office chemistry chemists chert chloride colloidal colour compounds concentration containing copper crystallisation determined dilute dissolved distilled dyes dysprosium effect Engineering erbium evaporated experiments Explosives Farringdon Street ferric filtered fractions glass grains grms heat holmium hydrochloric acid hydrogen hydrogen peroxide hydroxide increase industry Institution iron J. J. THOMSON laboratory lead liquid London manufacture material matter metal method mixture molar Newcastle Street nickel nitrate nitric acid nitrile nitrogen obtained oxide oxidising paper peroxide phosphate potassium precipitate present production Prof pure pyrites reaction reagent Research salt samples scientific Society sodium sodium hydroxide soil soluble solution starch steel substances sulphate sulphide sulphuric acid superphosphate supply Table temperature tion toluene trinitrotoluene velocity volume weight zinc ΙΟ